Synthesis of Monophasic Al3BC3 Powder with Hexagonal Plate-like Morphology

Maki, R. S. S. Matsumura, S. Kida, S. Maeda, T. Taira, H. Kusano, Y.

This paper describes the formation mechanism of monophasic Al3BC3 powder with hexagonal plate-like morphology using Al, B4C, and C powders in a stoichiometric ratio. For the synthesis of pure Al3BC3 by the conventional solid-state reaction method, it is important to avoid contamination from the starting powders. Thermogravimetry-differential thermal analysis curves and quantitative analysis by inductively coupled plasma-atomic emission spectroscopy revealed that there was no vaporization of the powder mixture during heating up to 1470 degrees C in a high-purity argon atmosphere. We found that the phases and Al3BC3 particle morphology after heating at 1800 degrees C strongly depended on the mixing conditions. In the case of a two-step process (remixing and reheating the sample), particles with random morphology were observed. On the other hand, well-faceted Al3BC3 particles were predominantly formed in a one-step process that involved heating after ball-milling for 24 h.

Inorg Chem

8

61

3493

3497